Polyamide-polyarlene sulfide blends

ABSTRACT

Polymer blends comprise a crystalline polyphthalamide component having high heat deflection temperature when filled with glass fibers and a polyarylene sulfide component.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a continuation-in-part of application Ser. No. 07/784,763, filed Oct. 30, 1991, and now abandoned which was a continuation of application Ser. No. 07/252,400, filed Sept. 30, 1988 and now abandoned, which was a CIP of application Ser. No. 07/060,456 filed Jun. 11, 1987 and now abandoned, which is incorporated herein by reference.

BACKGROUND OF THE INVENTION

This invention relates to blends comprising certain polyamides and polyarylene sulfides. More particularly, the invention relates to a blend of a polyarylene sulfide preferably a polyphenylene sulfide with a polyterephthalamide which, when filled with glass fibers, has a heat deflection temperature at 264 psi, according to ASTM D-648, above about 240° C., and to the corresponding filled blends containing fibrous or particulate fillers, preferably glass fibers.

Polyphthalamide compositions which, when filled with glass fibers and molded, have heat deflection temperatures at 264 psi, determined according to ASTM D-648, above about 240° C. are disclosed in the art. Among such polyphthalamides are polymers comprising recurring terephthalamide units, preferrably in combination with one or more other carboxylamide units, for example, adipamide or isophthalamide units. Compositions comprising such polyphthatamides, including particulate-filled and fiber-filled compositions, exhibit desirable thermal properties including high deflection temperature as well as high tensile strength and flexural modulus and are useful in various applications including preparation of molded articles, fibers, and laminates. Such compositions have utility in various applications, the neat and fiber-filled compositions being particularly suited for extrusion and molding applications.

Although these polyphthalamides have found wide acceptability for a great variety of end uses, the art continues to seek materials exhibiting still further improvement in such characteristics as solvent resistance and resistance to thermal-oxidative degradation, sometimes also referred to as thermal endurance. Such improvements would lead not only to longer useful life of products where demanding environments are encountered such as in under-the-hood automotive parts, but also utility in additional applications with even more stringent requirements.

In general, it is known that modification of polymer properties may be achieved in various ways. Modification of the molecular structure of a given composition through the use of additional monomers in polymerization can lead to desirable improvements in some properties. However, the same often are accompanied by loss of other desirable properties and use of additional monomers is not always practical due to process considerations. Addition of other materials to a polymeric composition may lead to property improvements without complicating a polymerization process; however the effects of additives often are unpredictable and, again, improvements in some properties often are achieved at the expense of other properties. For example, addition of high strength fibers such as glass or graphite fibers to polyamides is known to improve mechanical properties, such as tensile strength and flexural strengths and moduli, but these improvements are achieved at the expense of ductility. Blending a given polymer with one or more other polymers may give blends with a combination of properties intermediate of those of the individual components; however, processing requirements often limit the number of candidates that can be blended with a given polymer in an attempt to attain desirable property modifications and properties of a blend may or may not reflect those of its components depending on compatibility of the components with each other, reactivity thereof under blending or processing conditions and other factors.

Polyarylene sulfides are well known thermoplastics that find use in molding applications. As reported in "Technical Information On Ryton® Polyphenylene Sulfide Resins And Compounds" published by Phillips Petroleum Company, Plastics Technical Center, commercial polyphenylene sulfides designated Ryton polyphenylene sulfide exhibit excellent dimensional stability, inherent flame retardancy, thermal stability, chemical resistance, desirable electrical properties and ease of processing.

Blends of certain polyamides with polyarylene sulfides for various purposes to obtain blends having modified properties relative to those of the neat resin(s) are disclosed in the art. Blends containing from 0.01 to 10 wt % polyarylene sulfides with semicrystalline polyamides such as nylon 6 and polyamides obtained by condensation of a dibasic acid such as adipic, sebacic or terephthalic acid and a diamine such as hexamethylene diamine or 1,12-dodecanediamine that have improved molding characteristics and reduced warpage of parts molded therefrom are disclosed in U.S. Pat. No. 4,292,416. According to the patentee, the polyarylene sulfide useful in these blends must have a higher melting point than that of the polyamide. Inclusion of conventional additives for polyarylene sulfides, such as lubricants, stabilizers, pigments, dyes, fillers and plasticizers, also is disclosed. The patentee speculates that the improved properties of the blends result from a nucleating effect on the polyamide component imparted by the polyarylene sulfide component whereby crystallinity of the polyamide increases and properties dependent on degree of crystallinity are enhanced. The patentee also discloses that nucleation of polyamides can be accomplished through use of other such higher melting polymers which, during cooling, solidify prior to the polyamides so as to provide sites for nucleation.

U.S. Pat. No. 4,528,335, also assigned to Phillips Petroleum Company, discloses blends of amorphous polyamides, i.e., those having less than about 20 percent crystallinity, with polyarylene sulfides melting at about 260° to about 400° C. at weight ratios of 0.1:100 to about 100:100 are disclosed in U.S. Pat. No. 4,528,335. The blends, described to have improved impact strength and reduced shrinkage and warpage, may also contain fillers such as glass and carbon fibers.

Blends of low viscosity, uncrosslinked polyarylene sulfides not suited for injection molding, an epoxy compound and, optionally, a thermoplastic resin having a viscosity of at least 1,000 poise are disclosed in U.S. Pat. No. 4,528,346. According to the patentee such blends exhibit improved melt stability relative to commercially available injection molding grade polyarylene sulfides. Included among the various thermoplastic resins disclosed to be suitable as the optional component are polyamides. Adding fibers and inorganic fillers to such blends is also described.

Published Japanese Patent Application No. 55-135160 discloses blends of polyphenylene sulfide with nylon, unsaturated polyester or polyphenylene oxide resins, such resins being used to increase fluidity of the polyphenylene sulfide without sacrifices in other properties. Blends with nylon 6 and nylon 66 are specifically disclosed as are blends that contain glass fibers.

International Patent Application No PCT/US82/01688 (International Publication No. WO 83/02121), discloses adding a small amount of polyacrylamide or polyamide to a polyarylene sulfide melting from about 260° to about 400° C. to obtain compositions that are less corrosive to metals than neat polyphenylene sulfide. Among the disclosed polyamides are nylon 4, nylon 6, nylon 66, nylon 9, nylon 10, nylon 11, nylon 12, nylon 610, nylon 6T (polyhexamethylene terephthalamide), poly(p-phenylene terephthalamide), poly(m-phenylene isophthalamide), poly(N-N-diphenyl-p-phenylene isophthalamide), and polyamides derived from bis(paminocyclohexyl)methane and a dicarboxylic acid such as dodecanedioic acid. In the examples, blends containing up to 1 weight percent polyamide are disclosed.

International Patent Application No. PCT/NL85/00046 (International Publication No. WO 86/03212), discloses blends containing 5 to 50 weight percent polyarylene sulfide and 95 to 50 weight percent polytetramethylene adipamide. Use of mixtures of polytetramethylene adipamide with other polyamides in such blends also is disclosed as are blends containing fibers and particulate fillers.

U.S. Pat. Nos. 3,354,129, 3,862,095 and 3,790,536 disclose arylene sulfide polymers and processes for preparing them. These patents mention that such polymers can be blended with various materials including other polymers.

While the patents and publications discussed above disclose various blends, they do not disclose blends of a polyphthalamide component and a polyarylene sulfide component wherein the polyphthalamide component comprises terephthalamide units and which, when filled with 33 weight percent glass fibers, has a heat deflection temperature at 264 psi, according to ASTM D-648, above about 240° C. Further, the art does not disclose or suggest that blends of such a polyphthalamide component and a polyarylene sulfide component would exhibit the properties achieved according to this invention.

The art also does not disclose or suggest blends according to the invention comprising a polyphthalamide of fast or intermediate crystallization rate, as indicated by heat deflection temperature at 264 psi according to ASTM D-648 above about 240° C. when filled with 33 weight percent glass fibers, and a polyarylene sulfide component. Further, contrary to the teachings or express requirements of the art, it is not a requirement that the polyarylene sulfide melting point exceed polyamide melting point in the practice of the invention, and the melting points of some polyphthalamides found suitable for use in blends according to this invention exceed those of the polyarylene sulfide component by at least about 15° C.

It is an object of this invention to provide blends of a polyphthalamide component comprising terephthalamide units and, optionally, isophthalamide units and adipamide units which, when filled with 33 weight percent glass fibers, has a heat deflection temperature at 264 psi, according to ASTM D-648, above about 240° C. and a polyarylene sulfide component, as well as filled compositions based thereon having utility in molding and other applications. A further object of the invention is to provide such blends in which properties such as water absorption, methanol resistance, thermal endurance or flame resistance are improved relative to those of the polyphthalamide component. Other objects of the invention will be apparent to persons skilled in the art from the following.

SUMMARY OF THE INVENTION

The blends of this invention contain a polyphthalamide component comprising terephthalamide units which, when filled with 33 weight percent glass fibers, has a heat deflection temperature at 264 psi, according to ASTM D-648, above about 240° C., and a polyarylene sulfide component. Advantageously, such blends exhibit desirable thermal degradation temperatures, methanol resistance, water absorption, limiting oxygen index, thermal endurance and mechanical properties.

Filled compositions based on such blends also exhibit additional desirable properties such as improved tensile and flexural strengths and high heat deflection temperatures, and the invention thus is also directed to such filled compositions.

The invented blends normally exhibit two distinct melting points and glass transition temperatures, indicating substantial immiscibility of the polyphthalamide and polyarylene sulfide components. Although the mechanical properties of the blends generally fall between those of the components, as is often the case in blends of immiscible components, for compositions containing low-to-moderate levels of the polyarylene sulfide component, significant improvements in solvent resistance and thermal endurance relative to the polyphthalamide component are realized. In such blends, the polyarylene sulfide component is present as a separate, dispersed phase distributed through a matrix or continuous phase of the polyphthalamide component; it was not expected that the presence of such a discontinuous phase in the polyphthalamide matrix would yield the degree of improvement in retention of mechanical properties after thermal aging or immersion in solvents achieved according to the invention.

DESCRIPTION OF THE INVENTION

Briefly, the invented blends comprise a polyphthalamide, more particularly a polyterephthalamide which, when filled with glass fibers, has a heat deflection temperature at 264 psi, according to ASTM D-648, above about 240° C. and a polyarylene sulfide. The blends of this invention will contain from about 1 to about 99 weight percent, preferably from 10 to 90 weight percent of the polyphthalamide component and, correspondingly, from about 99 to about 1 weight percent, preferably from about 90 to about 10 weight percent polyarylene sulfide component, such weight percents being based on the total weight of polyphthalamide and polyarylene sulfide components.

These blends may also be filled with fibrous or particulate materials such as glass, graphite, boron, ceramic and aramid fibers, glass beads, calcium carbonate, graphite powder, pumice and the like, and the fillers may be used alone or in any combination. Filled blends according to the invention are particularly desirable because they combine the desirable blend properties with the high strength and other properties imparted by the fibers or particulates. Typically, amounts of such fibers or particulates range up to about 60 weight percent based on weight of the filled composition. Preferably, about 10 to about 50 weight percent of fibers or particulates is used to achieve desirable improvements in strength, modulus and heat deflection temperature without substantial sacrifices in processability of the filled composition. Glass fibers are especially preferred for molding applications.

The polyphthalamide component of the invented blends comprises terephthalamide units, and may optionally include additional carboxylamide units such as, for example, units selected from the group consisting of isophthalamide units and adipamide units.

The terephthalamide units may be structurally represented by the formula A below, and the optionally included isophthalamide units and adipamide units, may be represented respectively by the formulas B and C below. ##STR1## wherein R, R₁ and R₂ are independently divalent hydrocarbyl radicals and, preferably, divalent aliphatic hydrocarbyl radicals of 2 to about 14 carbon atoms.

In the formulas A, B and C depicted hereinabove, R, R₁ and R₂ are divalent hydrocarbyl radicals which can be the same or different. Straight chain, branched and cyclic aliphatic radicals and aromatic radicals are suitable. Preferably, R, R₁ and R₂ comprise an aliphatic radical of about 4 to about 20 carbon atoms, e.g., tetramethylene, hexamethylene, decamethylene, dodecamethylene and the like, alkyl-substituted aliphatic radicals such as methylpentamethylene, trimethylhexamethylene and the like, and cycloaliphatic radicals such as cyclohexylene, dicyclohexylmethane and the like. Polyphthalamides containing such radicals exhibit desirable thermal properties and good melt processibility, and raw materials for such polyphthalamides are readily available. Best results are achieved when R, R1 and R2 comprise hexamethylene or hexamethylene and trimethylhexamethylene, and especially when R, R₁ and R₂ consist of hexamethylene.

A variety of suitable polyphthalamides based on various aliphatic diamines are commercially available, and their preparation is disclosed in detail in commonly assigned U.S. Pat. No. 4,603,166, issued Jul. 29, 1986, the teachings of which are incorporated herein by reference.

A preferred polyphthalamide component of the invented blends comprises a semicrystalline polyphthalamide of fast or intermediate crystallization rate based on at least one aliphatic diamine and terephthalic acid. Particularly preferred are polyphthalamides based on at least one aliphatic diamine and terephthalic acid, isophthalic acid and adipic acid or terephthalic acid and adipic acid in which the mole ratio of the dicarboxylic acid moieties in units A, B and C, as depicted in the above formulas, is about 50-95:25-0:35-5, with about 65-75:25-15:10 being more preferred. Particularly preferred among such polyphthalamides are those wherein R, R₁ and R₂ in the above formulas comprise hexamethylene. Highly desirable polyphthalamides include those in which each of R, R₁ and R₂ is hexamethylene and the mole ratio of dicarboxylic acid moieties in the A, B and C units is about 65:25:10. Such polyphthalamides have melting points of about 305° to about 315° C. and generally have inherent viscosities of about 0.75 to about 1.4 dl/g, with about 1.0 to about 1.1 dl/g being preferred from the standpoint of melt stability and ease of processing. Heat deflection temperatures at 264 psi, according to ASTM D-648, of such polyphthalamides filled with 30-45 weight percent glass fibers and molded at about 120° C. generally range from about 480°-580° F. (250°-305° C.) as disclosed in U.S. Pat. No. 4,603,166.

Also disclosed therein and suitable as the polyphthalamide component of the invented blends are polyphthalamides of terephthalic acid, isophthalic acid and adipic acid compounds, in mole ratios of 65:35:0, 55:35:10, 60:30:10, 50:0:50 and 60:0:40, with hexamethylene diamine.

Among the polyphthalamides disclosed in U.S. Pat. No. 4,603,166, those melting at about 300° C. or greater are particularly suitable according to this invention. Generally, polyphthalamides based on terephthalic, isophthalic and adipic acids having mole ratios of the dicarboxylic acid moieties set forth above and aliphatic diamines of two to eight carbon atoms, i.e., polyphthalamides having recurring units corresponding to the above formulas wherein R, R₁ and R₂ are independently C₂₋₈ aliphatic radicals, melt above about 300° C. Specific examples of such diamines include tetramethylene diamine, pentamethylene diamine and hexamethylene diamine. Mixtures of aliphatic diamines of up to eight carbon atoms also can be employed as can mixtures of one or more such diamines with minor amounts of higher aliphatic diamines, e.g., those having nine to twelve carbon atoms. Generally, as terephthalamide content of such polyphthalamides increases, greater amounts of such higher aliphatic diamines and larger diamines can be used to obtain polyphthalamides that melt above about 300° C.

Another suitable example is the polyphthalamide of terephthalic acid, isophthalic acid and adipic acid in a mole fraction of 55/15/30 with hexamethylene diamine disclosed in Table 10 of published European Patent Application No. 84300744.4 (Publication No. 0121984). Especially preferred polyphthalamides are those wherein the heat deflection temperatures at 264 psi according to ASTM D-648 well in excess of about 240° C. when filled with 33 weight percent glass fibers and having glass transition temperatures less than 100° C. such that molding of the filled compositions to achieve such heat deflection temperatures can be carried out using steam-heated molds as opposed to more costly hot oil-heated systems. Mechanical properties, including tensile and flexural strength and modulus, of such polyphthalamides, particularly when filled with fibers or particulates, especially about 10 to about 60 weight percent glass fibers, together with their melt processibility and low water absorption tendencies (e.g., in the case of the 33 weight percent glass fiber filled polyphthalamides, water absorption generally is less than about four weight percent after immersion in boiling water for 120 hours) and good retention of mechanical properties when wet, make such polyphthalamide compositions particularly well suited as injection molding materials.

Also suitable as the polyphthalamide component of the invented blends are polyphthalamides prepared from dicarboxylic acid compounds comprising terephthalic acid and isophthalic acid compounds in a mole ratio of 80:20 to about 99:1 and hexamethylene diamine, optionally including additional diamines such as trimethylhexamethylene diamine in a mole ratio of about 98:2 to about 60:40. Such polyphthalamides, when filled with 33 weight percent glass fibers, have heat deflection temperatures at 264 psi according to ASTM D-648 of at least about 240° C. and are described in detail in commonly assigned U.S. Pat. No. 4,617,342, the teachings of which are incorporated herein by reference. Such polyphthalamides can offer advantages in terms of their extremely high heat deflection temperatures at 264 psi when filled with glass fibers and low water absorption due to an absence of adipamide units; however, melting points of such polyphthalamides are quite high, making melt processing more difficult.

Generally, it will be seen that suitable polyphthalamides may comprise units selected from the group consisting of terephthalamide, isophthalamide and adipamide units having mole ratios of dicarboxylic acid moieties in the units A, B and C in the above formulas within the broad ranges of 40-99:0-35:0-60, the proportions of the terephthalamide, isophthalamide and adipamide units as are present and the radicals R, R₁ and R₂ as represented in formulas A, B and C above being such that the heat deflection temperature of the polyphthalamide, when filled with 33 weight percent glass fibersand determined at 264 psi according to ASTM D-648, is at least about 240° C.

While precise relationships between composition and heat deflection temperature are not fully understood, a number of general principles provide guidance in providing polyphthalamides of suitable composition and properties for purposes hereof. Generally, melting temperature, rate of crystallization and level of crystallinity in copolyamides of terephthalic acid, isophthalic acid compounds and hexamethylene diamine increase with increasing terephthalamide to isophthalamide mole ratios, other things being equal. Heat deflection temperature at 264 psi according to ASTM D-648 of such copolyamides, when filled with 33 weight percent glass fibers, also increases with increased terephthalamide to isophthalamide mole ratios. Similarly, increasing heat deflection temperatures of glass-filled compositions at increasing terephthalamide plus adipamide to isophthalamide mole ratios in their terpolyamides with hexamethylene diamine can be seen from the aforementioned, commonly assigned U.S. Pat. No. 4,603,166. Yu et al., J. Poly. Sci., 42, 249 (1960) report that adipic acid and terephthalic acid are isomorphous in certain copolyamides, including those with hexamethylene diamine, such that replacement of terephthalic acid with adipic acid results in little change in melting point, although the authors acknowledge inability to prepare high terephthalic acid content copolyamides due to decomposition during the attempted preparations. Yu et al. also reports that crystallinity of polyamides decreases with increased branching of diamines used in preparation thereof, other things being equal.

Without wishing to be bound by theory, it appears that in the case of poly(hexamethylene phthalamides) consisting of at least two recurring units selected from the group consisting of hexamethylene terephthalamide, hexamethylene isophthalamide and hexamethylene adipamide units, there is a certain proportion of isophthalamide units, i.e., dicarboxylic acid moieties in units B in the above formulas, at or below which the polyphthalamides exhibit sufficient crystallinity and sufficiently high rates of crystallization during molding using a mold heated to at least Tg but below the melt crystallization temperature of the polyphthalamide that heat deflection temperatures at 264 psi, according to ASTM D-648, of the 33 weight percent glass fiber-filled compositions are normally at least about 240° C. Above a somewhat greater proportion of hexamethylene isophthalamide units, crystallinity and rates of crystallization are so low that the so-determined heat deflection temperatures of the 33 weight percent glass fiber-filled compositions normally are less than about 240° C. Between these levels of isophthalamide units, the so-determined heat deflection temperatures of the 33 weight percent glass fiber-filled compositions are normally at least about 240° C. provided that the remaining units of the composition include hexamethylene terephthalamide units and the mole ratio of hexamethylene terephthalamide units to hexamethylene isophthalamide units is high enough.

More specifically, such poly(hexamethylene phthalamides) consisting of about 19 to about 35 mole percent hexamethylene isophthalamide units based on total amide units, i.e., wherein the dicarboxylic acid moieties in units corresponding to the formula B above are about 19 to about 35 mole percent of the total dicarboxylic acid moieties, when filled with 33 weight percent glass fibers and molded using a mold heated above Tg but below Tcm normally have heat deflection temperatures at 264 psi according to ASTM D-648 of at least about 240° C. when the mole percentage of hexamethylene terephthalamide units (i.e, dicarboxylic acid moieties in units corresponding to formula A above) is at least about four times the mole percent hexamethylene isophthalamide units minus 75 percent. At hexamethylene isophthalamide unit contents in the upper portion of the aforesaid range of about 19 to about 35 mole percent, use of nucleants, higher mold temperatures, annealing and other techniques for promoting crystallization can be employed to facilitate attainment of heat deflection temperatures at 264 psi of at least about 240° C. according to ASTM D-648 in respect of the 33 weight percent glass fiber-filled polyphthalamides. Below about 19 mole percent hexamethylene isophthalamide units, heat deflection temperatures at 264 psi according to ASTM D-648 of the so-filled and so-molded compositions normally exceed about 240° C. whether the remaining units are all hexamethylene terephthalamide units, all hexamethylene adipamide units or a combination of hexamethylene terephthalamide units and hexamethylene adipamide units in any proportion. Above about 35 mole percent hexamethylene isophthalamide units, the poly(hexamethylene phthalamides) normally are amorphous or so slow to crystallize that the requisite heat deflection temperature at 264 psi according to ASTM D-648 normally is not attained even with the use of nucleating agents, annealing or high temperature molds. Thus, polyphthalamides comprising at least two recurring units selected from the group consisting of terephthalamide, isophthalamide and adipamide units which, when filled with 33 weight percent glass fibers, have heat deflection temperatures according to ASTM D-648g of at least about 240° C. include poly(hexamethylene phthalamides) consisting of at least two recurring units selected from the group consisting of hexamethylene terephthalamide, hexamethylene isophthalamide and hexamethylene adipamide units wherein the mole percent of the dicarboxylic acid moieties in the hexamethylene isophthalamide units based on total dicarboxylic acid moieties is 0 to about 35 mole percent; provided that when the mole percent of dicarboxylic acid moieties in the hexamethylene isophthalamide units is about 19 to about 35 mole percent, the mole percentages of dicarboxylic acid moieties in the hexamethylene terephthalamide, hexamethylene adipamide and hexamethylene isophthalamide units based on total dicarboxylic acid moieties (referred to below as M_(T), M_(A) and M_(I), respectively) satisfy the following formulas:

    M.sub.T ≧(4×M.sub.I)-75%                      (1)

    M.sub.T +M.sub.I +M.sub.A =100%                            (2)

Other suitable polyphthalamide compositions, for example, those based on diamines other than or in addition to hexamethylene diamine or comprising, in addition to recurring units selected from terephthalamide, isophthalamide and adipamide units, other dicarboxylic acid amide units, can be employed if desired, suitability of specific compositions being easily determined based on heat deflection temperatures at 264 psi of the 33 weight percent glass-filled compositions according to ASTM D-648 using a mold heated to above Tg but below Tcm of the polyphthalamide.

The polyphthalamides useful in the practice of this invention may be also described as having a fast or intermediate rate of crystallization. For purposes hereof, such polyphthalamides are characterized as fast crystallizing if the heat deflection temperature at 264 psi according to ASTM D-648 of the polyphthalamide composition filled with 33 weight percent glass fibers and molded using a mold heated above the glass transition temperature ("Tg") but below the melt crystallization temperature ("Tcm") of the polyphthalamide normally is at least about 240° C. and heat deflection temperature at 66 psi according to ASTM D-648 of the untilled polyphthalamide molded using a so-heated mold normally is at least about 220° C. Intermediate crystallizing polyphthalamides, for purposes hereof, are characterized by heat deflection temperatures at 264 psi according to ASTM D-648 normally of at least about 240° C. when so-filled and molded and heat deflection temperatures at 66 psi according to ASTM D-648 normally below about 220° C. in the case of the so-molded, unfilled compositions. Polyphthalamides with heat deflection temperatures at 264 psi according to ASTM D-648 normally below about 240° C. when so-filled and injection molded are slow-crystallizing or amorphous polyamides and are not suitable according to this invention because blends thereof with polyarylene sulfides exhibit low heat deflection temperatures and have poor chemical resistance unless polyarylene sulfide content of the blends is very high. Further, the slow crystallizing polyphthalamides can undergo crystallization during use at elevated temperatures of articles fabricated therefrom, resulting in dimensional change and premature failure.

While the polyphthalamide component of the invented blends is described herein in terms of heat deflection temperature of at least about 240° C. when filled with 33 weight percent glass fibers, it will be understood that such heat deflection temperatures often are also achieved at different fiber levels, the 33 weight percent level being chosen as a convenient reference point. Glass fibers of the type commonly utilized to prepare glass fiber-filled polyamide compositions suitable for injection molding can be used in the determination of heat deflection temperature. Compounding of such glass fibers with the polyphthalamide is conducted so that substantially uniform dispersion of fibers in the polyphthalamide is achieved. It also will be understood that heat deflection temperatures of the 33 weight percent glass fiber-filled polyphthalamide component of the invented blends can vary with molding conditions, including mold temperature and, to a lesser extent, cycle time, barrel temperature and injection pressure. Accordingly, while the polyphthalamide component of the invented blends is defined in terms of a heat deflection temperature at 264 psi according to ASTM D-648 in respect of the 33 weight percent glass fiber-filled resin, it will be understood that resins having the specified heat deflection temperatures under appropriate conditions are suitable according to this invention even though molding conditions may be varied to avoid attaining such heat deflection temperatures. As indicated above, heat deflection temperatures of at least about 240° C. normally are attained using a mold heated to above Tg but below Tcm of the polyphthalamide for 33 weight percent glass fiber-filled compositions containing the polyphthalamides suitable according to this invention. Use of nucleants and annealing also can facilitate achieving the specified heat deflection temperatures. Suitable glass fibers, compounding and molding conditions are illustrated in the examples appearing hereinbelow.

The polyphthalamide component of the invented blends may be selected from among the variety of commercially-available polyphthalamides such as the A-1000 and A-4000 grades of Amodel® polyphthalamide resins available from Amoco Polymers, Inc. and the Arlen resins supplied by the Mitsui Company. Other suitable polyphthalamides including polyterephthalamides have been disclosed in the art and these may also be or become available from commercial sources. Alternatively, the polyphthalamides may be prepared from the appropriate starting materials, e.g., dicarboxylic acids or their derivatives and diamines, in suitable proportions by any suitable means. As disclosed in U.S. Pat. No. 4,603,166, one such preparation involves a salt preparation step, preferably conducted batchwise to achieve proper stoichiometry, wherein dicarboxylic acid compounds, diamine and solvent are added to a suitable reaction vessel in appropriate amounts and maintained under conditions effective to cause salt formation but avoid appreciable conversion of salts to oligomers. Water is a preferred solvent and temperature is preferably maintained below about 120° C. to minimize conversion. Product of the salt preparation step can be introduced into a condensation section operated either batchwise or in continuous mode. In the condensation section substantial conversion of salts to polymer takes place. The condensation product then typically is introduced into a finishing section, such as a twin-screw extruder, to obtain further conversion and generally increase inherent viscosity from a level of about 0.1 to about 0.6 dl/g achieved in the condensation section up to about 0.8 dl/g or greater. The polymeric product can be recovered from the finishing section and, for example, pelletized or mixed with fillers, additives and the like. Commonly assigned U.S. Pat. No. 4,603,193 also is directed to preparation of such polyamides.

Polyarylene sulfides suitable for use in the blends according to the invention are those having a melting point up to about 285° C. and comprising in their molecules recurring arylene sulfide groups. Such materials and preparation thereof are widely known and are disclosed in the art, for example, in U.S. Pat. No. 3,354,129, issued Nov. 1, 1967, U.S. Pat. No., 790,536, issued Feb. 5, 1974, and U.S. Pat. No., 862,095, issued Jan. 21, 1975, each of which is incorporated herein by reference. Generally, polyarylene sulfides can be prepared from polyhalo-substituted aromatic compounds, such as 1,4-dichlorobenzene, and a suitable sulfur containing compound such as sodium sulfide, sodium hydrosulfide or hydrogen sulfide, at elevated temperature in a polar, organic solvent. Preferably, the polyarylene sulfide comprises a polyphenylene sulfide. More preferably an injection moldable polyphenylene sulfide melting at about 260° to about 280° C. is used. Specific examples of polyphenylene sulfides suitable for the purposes of this invention are those disclosed and sold commercially for injection molding applications, including Ryton® P4 Polyphenylene Sulfide manufactured by Phillips Petroleum Company and Tophren® T4 Polyphenylene Sulfide manufactured by Tophren Company, Ltd. These materials generally are available commercially in powder or pellet form, either being suitable for the present invention. Commercially available fiber-filled grades of polyphenylene sulfides may also be used to prepare fiber-filled blends according to this invention.

As noted, the blends of this invention may contain from about 1 to about 99 weight percent of the polyphthalamide component and, correspondingly, from about 99 to about 1 weight percent polyarylene sulfide component, based on the total weight of polyphthalamide and polyarylene sulfide components. Preferably, the polyarylene sulfide content of the invented blends will be greater than about 10 weight percent since for lower levels of polyarylene sulfide little change in properties relative to those of the polyphthalamide component is seen. More preferably, polyphthalamide component content is about 70 to about 90 weight percent and polyarylene sulfide component content is about 10 to about 30 weight percent because desirable mechanical properties of the polyphthalamide component are retained in the blends with significant improvements in solvent resistance and thermal endurance. For blends containing small amounts of the polyphthalamide component, and particularly at levels below about 10 wt %, there is little benefit to blend properties.

The blends according to this invention may be prepared by any suitable means. Conveniently, polyphthalamide and polyarylene sulfide components in powder or pellet form are melt blended in desired amounts at temperatures effective to render the blend components molten without degradation thereof in a high shear mixer, e.g., a twin-screw extruder, to obtain a desirably uniform blend. In view of the immiscibility of the blend components, use of kneading blocks or other suitable mixing elements is preferred in order to achieve a high degree of dispersion of the components. To minimize degradation of the blend and its components, preferred temperatures when using a twin-screw mixer are equal to or up to about 20° C. greater than the melting point of the highest melting component of the blends. Blending of the components in solid form, such as powder or pellets, prior to melt blending can be conducted to facilitate melt blending. Particulates and fibers can be incorporated into one or more of the blend components prior to blending them or into the blends by physical mixing with the blends in powder or pellet form and then extrusion compounding the result, by feeding the particulates or fibers to the molten blend in an extruder or other compounding apparatus or by other suitable methods. Blending of polyphthalamide and polyarylene sulfide components and incorporation of particulates or fillers can be accomplished in a single pass through an extruder or other suitable apparatus by mixing and blending the polymeric components in an upstream section of the equipment and then adding the fibers or fillers to the molten, blended components in a downstream portion of the equipment.

The invented blends also may contain pigments, stabilizers, flame retardants, nucleating agents, lubricants, impact modifiers and other suitable additives to improve or modify blend properties. A preferred heat stabilizer package is a combination of potassium iodine and cupric acetate.

Such blends may be found particularly useful as unfilled and filled injection molding compounds for production of molded objects such as electronic connectors, switch components, pump housings, valve components and under-the-hood automobile parts. Injection molding, extrusion and similar fabriction of the blends will generally be conducted using standard processing equipment conventionally employed in the art for such purposes. The invented blends may also be formed into fibers or films, including film laminates by conventional processing operations, and may be conveniently employed as matrix materials or binders in the fabrication of composite or laminated structures.

The present invention is described further in connection with the following examples, it being understood that the same are for purposes of illustration. In the examples and tables, examples of blends according to the invention are designated by Arabic numerals, comparative examples are designed by Roman numerals, with blends according to those comparative examples being designated by capital letters. Neat resins used in the blends of the examples and comparative examples also are designated by capital letters.

EXAMPLE 1

Polyphthalamide components A, B and C, were prepared from terephthalic acid, isophthalic acid, adipic acid and hexamethylene diamine in a mole ratio of about 65:25:10:100 as follows:

To a large, stainless steel, stirred reactor having an oil jacket heating system were added quantities of a 70-80 wt. % solution of hexamethylene diamine in water, adipic acid, isophthalic acid and terephthalic acid. About one mole percent benzoic acid, based on total moles of diamine and diacids, was added as a capping agent. Temperature increased during addition of the acids to 70° C. 800 parts per million sodium hypophosphite catalyst then were added to the reactor after which it was sealed, purged with nitrogen, leaving a 5.64 kg/cm₂ (80 psig) nitrogen blanket in the reactor, and then heated to about 120° C. and held at that temperature. A second such reactor was charged, purged and heated in like manner and the two reactors were used in parallel to provide continuous feed of salt solution to downstream processing by alternating between the two reactors.

Contents of the salt reactors were pumped continuously to a jacketed, oil-heated, stirred tank and maintained under pressure of 12.7 kg/cm₂ (180 psig) therein using a microprocessor-controlled Research Control Valve. The reactor was heated to about 220° C. Residence time in the reactor under such conditions was about 15 minutes, resulting in decrease in water content from about 35 wt. % based on weight of the materials in the initial charge to about 15 wt. % based on weight of material exiting the stirred tank.

Contents of the tank were pumped continuously to and through two jacketed, oil heated, stainless steel pipes of 0.95 cm inner diameter and lengths of 274 and 401 cm in series at a rate of about 8.2 kg/hour using a dual headed Bran-Lubbe piston pump. The first pipe was maintained at about 315°-325° C. and the second at about 325°-335° C. both under pressure of about 128 kg/cm₂ (1820 psi).

Contents of the second heated pipe were passed continuously through the Research Control Valve to a jacketed tube of about 0.94 cm inner diameter and about 274 cm length, equipped with thermocouples to monitor temperatures in the tube and between the outer wall of the tube and inner wall of the jacket, under pressure of about 7.8 kg/cm₂ (110 psig) with 325°-345° C. heat exchange fluid circulating in the heating jacket. Flashing of volatiles in the feed to the tube occurred in an upstream portion thereof.

Contents of the tube, comprising water vapor and molten polymer, were introduced onto the screws of a Werner and Pfleiderer Corporation ZSK-30, twin-screw extruder. Volatiles were allowed to escape through a rear vent in the extruder barrel. Polymer was conveyed between screw flights with the screws rotating at 100 rpm and the extruder barrel heated at 300° to 330° C. Polymer was extruded through a strand die of about 0.24 cm diameter, passed into a water bath and then chopped into pellets. Inherent viscosity of the resulting polyphthalamide, identified hereinbelow as A, was about 0.88 dl/g. Melting point was 312° C. Melt crystallization temperature was 270° C.

Polyphthalamide B was prepared substantially as described above except that pressure in the tube was slightly higher and temperature of the heat exchange fluid circulated around the tube was about 300° -345° C. Inherent viscosity was about 0.98 dl/g and melting point was 310° C. Melt crystallization temperature was 260° C.

Polyphthalamide C was prepared substantially as described above except pressure in the two pipes in series was about 151 kg/cm₂ (2150 psig) and pressure in the tube was about 6.4 kg/cm₂ (90 psig). Inherent viscosity was about 0.87 dl/g and melting point was 304° C. Melt crystallization temperature was 264° C.

While polyphthalamides A, B and C were of like composition and prepared similarly, mechanical properties of Polyphthalamide A were generally lower than those of Polyphthalamides B and C, as can be seen from Tables 1 and 4-6 below, for unknown reasons. Mechanical properties of Polyphthalamides B and C are more representative of those of the 65:25:10 hexamethylene terephthalamide, hexamethylene isophthalamide, hexamethylene adipamide polyphthalamides than those of Polyphthalamide A.

EXAMPLE 2

A blend of ten parts by weight of a commercially available polyphenylene sulfide powder, identified as Ryton P4 from Phillips Petroleum Company and having a melting point of 277° C., with ninety parts by weight of Polyphthalamide A from EXAMPLE 1 was prepared by physically mixing 150 grams of the polyphenylene sulfide and 1350 grams of the polyphthalamide in a sealed bucket and tumbling the bucket for about 3 minutes. The mixture was fed to a Werner & Pfleiderer Corporation ZSK-30 twin-screw extruder at a rate of about 75 grams/minute. Extruder operating conditions and barrel temperature profile were as follows:

    ______________________________________                                                     Barrel Temperatures (°C.)                                   Zone          Setting Indicated                                                ______________________________________                                         1              79     113                                                      2             149     158                                                      3             204     213                                                      4             299     301                                                      5             299     303                                                      6             299     301                                                      7             299     306                                                      8             299     300                                                      ______________________________________                                          Melt Temperature: 293° C.                                               Screw Speed: 50 rpm                                                            Screw Torque: 20%                                                        

Screw configuration in the extruder consisted of sections having relatively long pitch in zones 1 and 2, spike-like sections in zone 3, compression sections in zones 4 and 5 and sections of longer pitch in zones 6 and 7. Gas present in the polymer melt was allowed to escape from the extruder barrel through a vent port located in zone 7.

The molten blend exited the extruder through a strand die having a circular, 0.24 cm diameter orifice. The extrudate was cooled and chopped into pellets as in EXAMPLE 1.

Subsequently, the pellets were dried in a pumped vacuum oven at 110° C. (230° F.) and 0.35 mm Hg for 24 hours and then injection molded into test bars using an Arburg Injection Molding Machine operated as follows:

    ______________________________________                                         Mold Temperature Setting:                                                                       93° C.                                                 Rear Zone Setting:                                                                              293° C.                                                Front Zone Setting:                                                                             304° C.                                                Nozzle Setting:  304° C.                                                Injection Pressure:                                                                             21-42 kg/cm.sub.2                                             Holding Pressure:                                                                               18-28 kg/cm.sub.2                                             Back Pressure:   3.5-7 kg/cm.sub.2                                             Screw Speed:     160-180 rpm                                                   Injection Speed Setting:                                                                        5                                                             Injection Time Setting:                                                                         10 seconds forward, 20 seconds                                                 hold                                                          Total Cycle Time:                                                                               44 seconds                                                    ______________________________________                                    

Physical properties of the test bars were determined according to the following methods:

    ______________________________________                                         Tensile Properties  ASTM D-638 Type I test                                     (including Ultimate Tensile Strength                                                               bars tested at                                             ("UTS") and Elongation at Break):                                                                  5 cm/minute);                                              Flexural Properties:                                                                               ASTM D-790;                                                Notched Izod Impact Strength:                                                                      ASTM D-256;                                                Tensile Impact Strength:                                                                           ASTM D-1822                                                                    (type S test bars);                                        Heat Deflection Temperature                                                                        ASTM D-648;                                                ("HDT"):                                                                       Water Absorption:   ASTM D-570;                                                Methanol Exposure   ASTM D-543;                                                Limiting Oxygen Index (LOI):                                                                       ASTM D-2863;                                               Glass Transition Temperature (Tg),                                                                 Pellets tested by                                          Melting Temperature (Tm) and Melt                                                                  Differential Scanning                                      Crystallization Temperature (Tcm):                                                                 Calorimetry at 20° C./                                                  minute.                                                    Degradation Temperature:                                                                           Pellets tested by Thermal                                                      Gravimetric Analysis at a                                                      10° C./minute scan rate                                                 under nitrogen                                             ______________________________________                                    

Test results are reported in TABLE 1 below. In accordance with the ASTM test methods identified above, an average of results for the number of samples specified in the test methods is reported in TABLE 1 and subsequent tables.

EXAMPLES 3-4

Following essentially the procedure of EXAMPLE 2, a series of compositions was prepared from the materials used in that example but with variations in levels of polyphenylene sulfide and polyphthalamide components. Samples of neat polyphthalamide A from EXAMPLE 1 and neat polyphenylene sulfide used in EXAMPLES 2-4 also were processed in the ZSK-30 twin -screw extruder essentially as in EXAMPLE 2 to provide comparable thermal history. Test bars were molded from the blends and neat resins according to the procedure of EXAMPLE 2 and tested as described therein. Properties and molding conditions are reported in TABLE 1. In the table the neat polyphenylene sulfide is designated "D".

                  TABLE 1                                                          ______________________________________                                                 Example                                                                        A      2       3        4      D                                       ______________________________________                                         Polyphthal-                                                                              100/0    90/10   50/50  10/90  0/100                                 amide/Poly-                                                                    phenylene                                                                      Sulfide                                                                        (wt. %)                                                                        UTS (kg/cm.sub.2)                                                                        754      609      124*   321*  461                                   Elongation at                                                                            3.2      2.52       0.60                                                                                  1.26                                                                               1.47                                  Break (%)                                                                      Flexural  >1556    1184    747    740    719                                   Strength                                                                       (kg/cm.sup.2)                                                                  Flexural  33.5     35.9      38.5   40.5 44.7                                  Modulus                                                                        (× 10.sub.3 kg/cm.sup.2)                                                 Notched Izod                                                                             3.3      3.1        1.8    1.3 1.1                                   (cm-kg/cm)                                                                     Tensile Impact                                                                           84       60       30     26    32                                    (cm-kg/cm.sup.2)                                                               HDT @ 264 psi                                                                            104      126     115    103    101                                   (°C.)                                                                   Limiting  24       24       33     40    40                                    Oxygen Index                                                                   (%)                                                                            Tg (°C.)                                                                          117      124     123                                                                    87       85     85    85                                    Tm (°C.)                                                                          312      313     307                                                                    281     280    279    277                                   Degradation                                                                              369      415     404    427    467                                   Temp. (°C.)                                                             Mold Temper-                                                                             93       93       93     93    93                                    ature (°C.)                                                             Barrel Temper-                                                                 ature (°C.)                                                             Rear Zone 310      293     293    293    282                                   Front Zone                                                                               318      304     304    304    288                                   Nozzle    318      304     304    304    288                                   ______________________________________                                          *These values are not representative because test bars broke at clamps of      the testing device.                                                      

EXAMPLES 5-7

Glass fiber-filled compositions were prepared from the blends of EXAMPLES 2-4 and the neat polyphthalamide and polyphenylene sulfide resins used to prepare such blends. The filled materials were prepared by grinding the blends or neat resins to about 2 mm particle size and then physically mixing the same with commercially available, 0.32 cm long glass fibers identified as PPG 3540 from PPG Industries, Inc., in amounts sufficient to yield filled compositions containing 33 wt. % glass fibers based on weight of the filled compositions. Physical mixing was accomplished using the bucket tumbler as in EXAMPLE 2. Test bars were molded under conditions shown in TABLE 2 and otherwise according to the procedure and under conditions of EXAMPLE 2. Test bars were evaluated as in EXAMPLE 2 and results are reported in TABLE 2.

                  TABLE 2                                                          ______________________________________                                                    Example                                                             Blend or Neat Resin                                                                         E       5       6     7     F                                     from Example A       2       3     4     D                                     ______________________________________                                         UTS (kg/cm.sup.2)                                                                           1909    2346    1402  1437  1564                                  Elongation at Break                                                                         4.0     3.8     2.2   2.5   2.7                                   (%)                                                                            Flexural Strength                                                                           2875    3396    2269  2494  2381                                  (kg/cm.sup.2)                                                                  Flexural Modulus                                                                            105     116     116   130   121                                   (× 10.sup.3 kg/cm.sup.2)                                                 Notched Izod 17.4    17.4    19.6  17.4  16.4                                  (cm-kg/cm)                                                                     Tensile Impact                                                                              228     231     129   162   160                                   (cm-kg/cm.sup.2)                                                               HDT @ 264 psi (°C.)                                                                  282     292     273   275   271                                   Mold Temperature                                                                            93      93      93    93    93                                    (°C.)                                                                   Barrel Temperature                                                             (°C.)                                                                   Rear Zone    310     310     310   310   310                                   Front Zone   321     321     321   321   321                                   Nozzle       321     321     321   321   321                                   ______________________________________                                    

EXAMPLES 8-10

Following essentially the procedure of EXAMPLE 2, blends were prepared from the Polyphthalamide A of EXAMPLE 1 and a polyphenylene sulfide, Tophren T-4 polyphenylene sulfide from Tophren Co. Ltd., having a melting point of 280° C. and designated as "G". Test bars were prepared and evaluated as in EXAMPLE 2; evaluation results and molding conditions are shown in TABLE 3. The neat resins were processed in the ZSK-30 extruder in similar manner to provide comparable thermal history.

                  TABLE 3                                                          ______________________________________                                                  Example                                                                        A      8       9       10     G                                       ______________________________________                                         Polyphthalamide/                                                                          100/0    90/10   70/30 50/50  0/100                                 Polyphenylene                                                                  Sulfide (wt. %)                                                                UTS (kg/cm.sup.2)                                                                         754      803     571    345*  486                                   Elongation at                                                                             3.2      3.7     2.5      1.4 1.8                                   Break (%)                                                                      Flexural Strength                                                                         >1556    1409    1310  860    1050                                  (kg/cm.sup.2)                                                                  Flexural Modulus                                                                          33.5     35.6    36.1    37.3 37.8                                  (× 10.sup.3 kg/cm.sup.2)                                                 Notched Izod                                                                              3.3      3.1     2.6      1.3 1.3                                   (cm-kg/cm)                                                                     Tensile Impact                                                                            84       93      86     45    39                                    (cm-kg/cm2)                                                                    HDT @ 264 psi                                                                             104      110     111   111    114                                   (°C.)                                                                   Tg (°C.)**                                                                         117      108     108   110    86                                    Tm (°C.)**                                                                         312      306     280   283    280                                   Degradation                                                                               369      412     409   407    414                                   Temp. (°C.)                                                             Water Absorption                                                                          0.66     0.58    0.44     0.26                                                                               0.06                                  (wt. % after 24                                                                hours)                                                                         Retained UTS                                                                              70       94      100   112    94                                    (% after 24 hrs in                                                             boiling MeOH)                                                                  Mold Temper-                                                                              93       93      93     93    104                                   ature (°C.)                                                             Barrel Temper-                                                                 ature (°C.)                                                             Rear Zone  310      310     310   310    282                                   Front Zone 318      318     318   318    288                                   Nozzle     318      318     318   318    288                                   ______________________________________                                          Notes:                                                                         *This value is not representative because test bars broke at clamps of th      testing device.                                                                **Second Tgs and Tms for the blends of Examples 8-10 were not observed.  

EXAMPLES 11-14

Following essentially the procedure of EXAMPLE 2, a series of blends was prepared from the polyphenylene sulfide used in EXAMPLE 2 and Polyphthalamide B from EXAMPLE 1. Test bars were prepared from the blends and the neat resins, processed in like manner to provide comparable thermal history, and tested as in EXAMPLE 2, results and molding conditions being reported in TABLE 4. Also reported in the table are results for test bars molded from a commercial pellet grade polyphenylene sulfide, Ryton R-6 Polyphenylene Sulfide from Phillips Petroleum Company. That material is designated "H" in the table

                                      TABLE 4                                      __________________________________________________________________________                            Example                                                                        B    11   12   13   14   D     H                        __________________________________________________________________________     Polyphthalamide/Polyphenylene Sulfide (wt. %)                                                         100/0                                                                               90/10                                                                               85/15                                                                               50/50                                                                               10/90                                                                               0/100 0/100                    UTS (kg/cm.sup.2)      916  845  754  358  339  368   390                      Elongation at Break (%)                                                                               4.1  3.2  2.8  1.3  1.1     1.2                                                                               1.6                      Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                       35.7 39.6 39.9 39.7 42.1   43.7                                                                               41.5                     Notched Izod (cm-kg/cm)                                                                               8.7  5.4  4.9  2.7  2.7     2.7                                                                               1.9                      Tensile Impact (cm-kg/cm.sup.2)                                                                       138  127  99   30   26    21   26                       LOI (%)                22   24   25   32   39    38   ND                       Tg (°C.)        118  121  123  119                                                                       87   84   83    85   85                       Tm (°C.)        310  313  312  307  277  279   271                                                  280  279  279                                      HDT @ 264 psi (°C.)                                                                            117  122  123  114  99    97   102                      Water Absorption (wt. % after 24 hours)                                                               0.72 0.66 0.60 0.30 0.09    0.03                                                                              ND                       Retained UTS (% after 24 hrs in boiling MeOH)                                                         72   68   73   ND*  82     68**                                                                               ND                       Mold Temperature (°C.)                                                                         93   93   93   93   93    93   93                       Barrel Temperature (°C.)                                                Rear Zone              310  293  293  293  293  277   293                      Front Zone             332  304  304  304  304  282   304                      Nozzle                 321  304  304  304  304  282   304                      __________________________________________________________________________      Notes:                                                                         *ND indicates that the property in question was not determined.                **This value is an average of five widely divergent test values. Retestin      gave an average value of 98% without significant divergence among              individual values.                                                       

EXAMPLES 15-18

EXAMPLES 11-14 were repeated except that the extruder was equipped with kneading blocks to promote better blending. Results and conditions are reported in TABLE 5.

                                      TABLE 5                                      __________________________________________________________________________                             Example                                                                        B    15   16   17   18   D                             __________________________________________________________________________     Polyphthalamide/Polyphenylene Sulfide (wt. %)                                                          100/0                                                                               90/10                                                                               85/15                                                                               50/50                                                                               10/90                                                                               0/100                         UTS (kg/cm.sup.2)       1099 887  817  263  433  440                           Elongation at Break (%) 5.82 3.75 3.33 0.92 1.42 1.34                          Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                        34.5 34.7 36.2 37.6 42.1 46.1                          Retained UTS (% after 24 hrs in boiling MeOH)                                                          67   73   76   76   79   95                            Notched Izod (cm-kg/cm) 7.8  5.0  3.7  0.87 0.87 0.87                          Tensile Impact (cm-kg/cm.sup.2)                                                                        155  67   32   35   28   30                            LOI (%)                 24   24   26   33   37   37                            HDT @ 264 psi (°C.)                                                                             116  118  116  105  104  100                           Tg (°C.)         104  115  113  116  119                                                             93   91   83   88   89                            Tm (°C.)         311  311  311  306                                                                  280  279  279  278  278                           Degradation Temp. (°C.)                                                                         398  410  401  398  392  462                           Mold Temperature (°C.)                                                                          93   93   93   93   93   93                            Barrel Temperature (°C.)                                                Rear Zone               310  293  293  293  293  277                           Front Zone              332  304  304  304  304  282                           Nozzle                  321  304  304  304  304  282                           __________________________________________________________________________

EXAMPLES 19-22

Following essentially the procedure of Example 2, a series of blends was prepared from Polyphthalamide C from Example 1 and Tophren T4 polyphenylene sulfide (different lot than used in EXAMPLES 8-10) melting at 275° C., designated "I" in TABLE 6. Test bars prepared in like manner in the ZSK-30 extruder as in Example 2 were evaluated; results and molding conditions are reported in TABLE 6.

                                      TABLE 6                                      __________________________________________________________________________                                Example                                                                        C    19   20   21   22   I                          __________________________________________________________________________     Polyphthalamide/Polyphenylene Sulfide (wt. %)                                                             100/0                                                                               90/10                                                                               70/30                                                                               50/50                                                                               10/90                                                                               0/100                      UTS (kg/cm.sup.2)          1036 965  599  437  540  561                        Elongation at Break (%)    4.7  4.5  2.5  1.6  2.0  2.2                        Retained UTS (% after 24 hours in boiling MeOH)                                                           63   63   89   85   96   100                        Retained UTS (% after 24 hours in 93° C. acetic acid)                                              56   54   85   88   99   99                         Notched Izod (cm-kg/cm)    4.4  4.9  1.1  1.1  1.1  1.1                        Tensile Impact (cm-kg/cm.sup.2)                                                                           86   84   60   54   54   60                         HDT at 264 psi (°C.)                                                                               112  115  103  100  101  102                        LOI (%)                    23   24   26   32   44   43                         Tg (°C.)            130  120  132  122  120                                                             102  80   88   103  85                         Tm (°C.)            304  307  308  307                                                                  278  277  276  277  275                        Mold Temperature (°C.)                                                                             93   93   93   93   93   93                         Barrel Temperature (°C.)                                                Rear Zone                  310  310  310  304  304  282                        Front Zone                 318  318  318  310  310  288                        Nozzle                     318  318  318  310  310  288                        __________________________________________________________________________

COMPARATIVE EXAMPLE I

A series of blends was prepared from the polyphenylene sulfide used in EXAMPLE 2 and a commercial nylon 66 identified as Celanese 1000-1. The blends were prepared as in EXAMPLE 2 except that the extruder setting temperature was 288° C. instead of 299° C. in zones 4-8.

Test bars were prepared from the blends and from the neat resins, processed in the ZSK-30 extruder in like manner, and tested as in EXAMPLE 2, results and molding conditions being shown in TABLE 7.

                                      TABLE 7                                      __________________________________________________________________________                            Example                                                                        J    K    L    M    N    D     H                        __________________________________________________________________________     Nylon/Polyphenylene Sulfide (wt. %)                                                                   100/0                                                                               90/10                                                                               85/15                                                                               50/50                                                                               10/90                                                                               0/100 0/100                    UTS (kg/cm.sup.2)      817  874  817  584  326  368   390                      Elongation at Break (%)                                                                               18.2 4.2  3.7  2.2  1.1     1.2                                                                               1.6                      Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                       34.0 35.2 35.4 39.1 43.1   43.7                                                                               41.5                     Notched Izod (cm-kg/cm)                                                                               5.5  4.4  4.9  3.3  2.7     2.7                                                                               1.9                      Tensile Impact (cm-kg/cm.sup.2)                                                                       127  108  101  43   20    21   26                       LOI (%)                25   25   26   33   37    38   ND                       Tg (°C.)        38   39   40   38   41                                                              83   84   81   85    85   85                       Tm (°C.)        261  260  260  258  252                                                                       279  279  279   271                      HDT @ 264 psi (°C.)                                                                            189  201  200  210  97    97   102                      Water Absorption (wt. % after 24 hours)                                                               1.27 1.23 1.16 0.70 0.12    0.03                                                                              ND                       Retained UTS (% after 24 hrs in boiling MeOH)                                                         42   30   32   50   77    68*  ND                       Mold Temperature (°C.)                                                                         93   93   93   93   93    93   93                       Barrel Temperature                                                             Rear Zone (°C.) 277  277  277  277  277  277   293                      Front Zone (°C.)                                                                               282  282  282  282  282  282   304                      Nozzle (°C.)    282  282  282  282  282  282   304                      __________________________________________________________________________      *This value is an average of five widely divergent test values. Retesting      gave 98% as noted in TABLE 4.                                            

EXAMPLES 23-25

Following essentially the procedure of EXAMPLE 1, a polyphthalamide having a melting point of 297° C., melt crystallization temperature of 245° C. and inherent viscosity of about 1.02 dl/g (hereinafter Polyphthalamide "O",) was prepared from terephthalic acid, isophthalic acid, adipic acid and hexamethylene diamine in a mole ratio of 60:15:25:100. Pressure in the jacketed tube was about 7.0 kg/cm₂ (100 psig), temperature of the circulating heat exchange fluid was about 335°-345° C. and extruder barrel temperature was 310°-320° C. Polyphthalamide 0 then was blended with varying amounts of polyphenylene sulfide of the type used in EXAMPLE 2 following essentially the procedure of that example and the blends and neat resins were tested. Results and molding conditions were as follows:

                  TABLE 8                                                          ______________________________________                                                    Example                                                                        O     23      24      25    D                                       ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           937     944     387   345   373                                   Elongation at Break                                                                         6.9*    4.0     1.4   1.1   1.2                                   (%)                                                                            Flexural Modulus                                                                            34.6    35.9    36.5  38.6  40.4                                  (× 10.sup.3 kg/cm.sup.2)                                                 Notched Izod 3.8     4.4     1.1   1.1   1.1                                   (cm-kg/cm)                                                                     Flexural Strength                                                                           1191    1479    874   803   867                                   (kg/cm.sup.2)                                                                  Tg (°C.)**                                                                           104     101     99    87    88                                    Tm (°C.)                                                                             307     307     305   305                                                              278     279   278   276                                   HDT @ 264 psi (°C.)                                                                  107     105     106   92    100                                   Degradation Temp.                                                                           372     372     391   382   427                                   (°C.)                                                                   Mold Temperature                                                                            93      93      93    93    93                                    (°C.)                                                                   Barrel Temperature                                                             (°C.)                                                                   Rear Zone    310     293     293   293   277                                   Front Zone   316     304     304   304   282                                   Nozzle       316     304     304   304   282                                   ______________________________________                                          *This is an average of six diverging measurements (7.4%, 9.6%, 10.6%,          3.8%, 3.3% and 6.3%). Reasons for such divergence are unknown.                 **Second Tgs for these specimens were not observed.                      

Solvent resistance of the blends from these examples were determined by measuring UTS of test bars before and after immersion in boiling (65° C.) methanol for 24 hours and in acetic acid at 93° C. for 24 hours and calculating retained UTS as a percentage of UTS before immersion. Solvent exposures were performed according to ASTM D-543. Results are shown in TABLE 9.

                  TABLE 9                                                          ______________________________________                                                    Example                                                                        O     23      24      25    D                                       ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           1106    902     317   366   416                                   UTS (kg/cm.sup.2) after                                                        24 hours in:                                                                   65° C. Methanol                                                                      672     591     334   244   361                                   93° C. Acetic Acid                                                                   451     381     331   365   404                                   Retained UTS (%)                                                               after 24 hours in:                                                             65° C. Methanol                                                                      61      66      105   67    87                                    93° C. Acetic Acid                                                                   41      42      104   100   97                                    ______________________________________                                    

COMPARATIVE EXAMPLE II

For purposes of comparison, a polyphthalamide of 50:50:100 terephthalic acid, isophthalic acid and hexamethylene diamine, corresponding to the description of the amorphous polyamide, Zytel 330, given in U.S. Pat. No. 4,258,335, was prepared following essentially the procedure of EXAMPLE 1 and then blended with polyphenylene sulfide following essentially the procedure of EXAMPLE 2. The blends were tested; results and molding conditions are reported in TABLE 10 in which the polyphthalamide is designated "P". Heat deflection temperature at 264 psi, according to ASTM D-648, of Polyphthalamide P compounded with 33 weight percent glass fibers as in Examples 5-7 and molded using a mold heated at 104° C. was 133° C.

                  TABLE 10                                                         ______________________________________                                                    Example                                                                        P     Q       R       S     D                                       ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           834     852     387   303   324                                   Elongation at Break                                                                         9.2*    4.9     1.6   1.0   1.1                                   (%)                                                                            Flexural Modulus                                                                            31.1    30.2    33.7  39.2  40.4                                  (× 10.sup.3 kg/cm.sup.2)                                                 Notched Izod 8.2     6.5     1.1   1.1   1.1                                   (cm-kg/cm)                                                                     Flexural Strength                                                                           NB**    NB**    831   768   852                                   (kg/cm.sup.2)                                                                  Tg (°C.)                                                                             125     130     86    93    91                                    Tm (°C.)                                                                             261     273     279   280   279                                   HDT @ 264 psi (°C.)                                                                  118     114     112   103   99                                    Degradation Temp.                                                                           396     384     404   410   418                                   (°C.)                                                                   Mold Temperature                                                                            93      93      93    93    93                                    (°C.)                                                                   Barrel Temperature                                                             (°C.)                                                                   Rear Zone    277     277     277   277   277                                   Front Zone   282     282     282   282   282                                   Nozzle       282     282     282   282   282                                   ______________________________________                                          *This is an average of six diverging measurements (3.3%, 6.7%, 6.5%, 6.5%      10.3% and 22.0%); reasons for the divergence are unknown.                      **Test specimens did not break or yield below 5% strain.                 

Comparing results in TABLE 10 with those reported in TABLES 1, 3-6 and 8 with respect to blends according to the invention it can be seen that there was generally a greater decline in mechanical properties, such as UTS and Notched Izod, of the comparative blends with increasing levels of polyphenylene sulfide than shown by the invented blends.

COMPARATIVE EXAMPLE III

For purposes of comparison, blends of polyphenylene sulfide of the type used in EXAMPLE 2 with a commercial polyphthalamide designated Zytel® 330 available from E. I. DuPont de Nemours Co. were prepared following essentially the procedure of EXAMPLE 2. Zytel 330 is believed to be an amorphous polyamide of 30:70 terephthalic acid and isophthalic acid with hexamethylene diamine plus a small amount of bis-p-aminocyclohexyl(methane). The blends were tested; results and molding conditions are reported in TABLE 11 in which the Zytel 330 is identified as "T." Heat deflection temperature at 264 psi according to ASTM D-648 of the Zytel 330 compounded with 33 weight percent glass fibers as in EXAMPLES 5-7 and molded using a mold heated at 104° C. was 129° C.

                  TABLE 11                                                         ______________________________________                                                    Example                                                                        T     U       V       W     D                                       ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           838     810     606   331   359                                   Elongation at Break                                                                         4.3     4.0     2.5   1.1   1.1                                   (%)                                                                            Flexural Modulus                                                                            30.8    30.3    33.4  37.9  39.8                                  (× 10.sup.3 kg/cm.sup.2)                                                 Notched Izod 4.9     4.4     2.2   0.5   0.5                                   (cm-kg/cm)                                                                     Flexural Strength                                                                           1339    1303    1240  705   852                                   (kg/cm.sup.2)                                                                  Tg (°C.)                                                                             130     131     87    89    88                                    Tm (°C.)                                                                             *       278     279   277   277                                   HDT @ 264 psi (°C.)                                                                  116     113     113   105   104                                   Degradation Temp.                                                                           379     395     398   403   427                                   (°C.)                                                                   Mold Temperature                                                                            93      93      93    93    93                                    (°C.)                                                                   Barrel Temperature                                                             (°C.)                                                                   Rear Zone    277     277     277   277   277                                   Front Zone   282     282     282   282   282                                   Nozzle       282     282     282   282   282                                   ______________________________________                                          *Polyphthalamide T lacked a definite melting point, indicating the             substantially amorphous nature thereof.                                  

Solvent resistance of these blends was determined as in EXAMPLES 23-25; results are reported in TABLE 12.

                  TABLE 12                                                         ______________________________________                                                    Example                                                                        T     U       V       W     D                                       ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           930     733     585   345   416                                   UTS (kg/cm.sup.2) after                                                        24 hours in:                                                                   65° C. Methanol                                                                      *       *       *     217   361                                   93° C. Acetic Acid                                                                   *       *       *     279   404                                   Retained UTS (%)                                                               after 24 hours in:                                                             65° C. Methanol                                                                      *       *       *      63    87                                   93° C. Acetic Acid                                                                   *       *       *      81    97                                   ______________________________________                                          *Specimens disintegrated and could not be tested.                        

Comparing the results in TABLES 11 and 12 with those in TABLES 1, 3-6, 8 and 9, it can be seen that the comparative, amorphous polyphthalamide component-containing blends and the invented blends, while generally comparable in mechanical properties, were considerably different in retention of ultimate tensile strength after exposure to methanol and acetic acid, the invented blends showing far superior property retention.

EXAMPLES 26-28

EXAMPLES 23-25 were repeated except that a different ZSK-30 extruder was used. Results and molding conditions are reported in TABLE 13.

                  TABLE 13                                                         ______________________________________                                                    Example                                                                        O     26      27      28    D                                       ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           993     909     395   359   324                                   Elongation at Break                                                                         4.4     3.8     1.4   1.2   1.1                                   (%)                                                                            Flexural Modulus                                                                            35.6    36.5    37.1  39.2  40.4                                  (× 10.sup.3 kg/cm.sup.2)                                                 Notched Izod 3.8     2.7     1.1   1.1   1.1                                   (cm-kg/cm)                                                                     Flexural Strength                                                                           1479    1515    852   845   852                                   (kg/cm.sup.2)                                                                  Tg (°C.)                                                                             104     102     105                                                                            86    88    91                                    Tm (°C.)                                                                             308     308     305                                                                            278   275   279                                   HDT @ 264 psi (°C.)                                                                  104     115     109   103   99                                    Degradation Temp.                                                                           386     380     391   375   418                                   (°C.)                                                                   Mold Temperature                                                                            93      93      93    93    93                                    (°C.)                                                                   Barrel Temperature                                                             (°C.)                                                                   Rear Zone    310     293     293   293   277                                   Front Zone   316     304     304   304   282                                   Nozzle       316     304     304   304   282                                   ______________________________________                                    

EXAMPLES 29-31

The blends prepared in EXAMPLES 23-25 and neat resins of the type used in those examples were dry blended with 33 weight percent glass fibers and the filled blends were molded and tested following essentially the procedure of EXAMPLES 26-28; results and molding conditions are shown in TABLE 14.

                  TABLE 14                                                         ______________________________________                                                    Example                                                             Blend or Neat Resin                                                                         X       29      30    31    Y                                     From Example 0       23      24    25    D                                     ______________________________________                                         Polyphthalamide/                                                                            100/0   90/10   50/50 10/90 0/100                                 Polyphenylene Sulfide                                                          (wt %)                                                                         UTS (kg/cm.sup.2)                                                                           1804    2078    1261  1233  1423                                  Elongation at Break                                                                         3.6     4.1     2.2   2.2   2.7                                   (%)                                                                            Flexural Modulus                                                                            100     102     106   116   118                                   (× 10.sup.3 kg/cm.sup.2)                                                 Flexural Strength                                                                           2755    2832    1853  2029  2071                                  (kg/cm.sup.2)                                                                  Notched Izod 14.2    14.2    15.8  14.7  10.4                                  (cm-kg/cm)                                                                     HDT @ 264 psi (°C.)                                                                  289     288     273   269   267                                   Mold Temperature                                                                            104     104     104   104   104                                   (°C.)                                                                   Barrel Temperature                                                             (°C.)                                                                   Rear Zone    310     293     293   293   277                                   Front Zone   316     304     304   304   282                                   Nozzle       316     304     304   304   282                                   ______________________________________                                    

COMPARATIVE EXAMPLE IV

The procedure of EXAMPLES 29-31 was repeated using the blends and neat resins of COMPARATIVE EXAMPLE II; results and molding conditions are shown in TABLE 15.

                                      TABLE 15                                     __________________________________________________________________________     Example            Z   AA  BB  CC  DD                                          Blend or Neat Resin From Example:                                                                 P   Q   R   S   D                                           __________________________________________________________________________     Polyphthalamide/Polyphenylene                                                                     100/0                                                                              90/10                                                                              50/50                                                                              10/90                                                                              0/100                                       Sulfide (wt %)                                                                 UTS (kg/cm.sup.2)  2106                                                                               2092                                                                               1324                                                                               1282                                                                               1381                                        Elongation at Break (%)                                                                           4.3 4.3 2.4 2.3 2.5                                         Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                   91.3                                                                               94.1                                                                               101 110 112                                         Flexural Strength (kg/cm.sup.2)                                                                   2733                                                                               2846                                                                               1909                                                                               1902                                                                               2015                                        Notched Izod (cm-kg/cm)                                                                           13.1                                                                               13.6                                                                               16.9                                                                               18.0                                                                               13.1                                        HDT @ 264 psi (°C.)                                                                        133 132 250 269 269                                         Mold Temperature (°C.)                                                                     104 104 104 104 104                                         Barrel Temperature (°C.)                                                   Rear Zone       282 282 282 282 282                                            Front Zone      288 288 288 288 288                                            Nozzle          288 288 288 288 288                                         __________________________________________________________________________

COMPARATIVE EXAMPLE V

The procedure of EXAMPLES 29-31 was repeated using the blends and neat resins of COMPARATIVE EXAMPLE III; results and molding conditions are shown in TABLE 16.

                                      TABLE 16                                     __________________________________________________________________________     Example            EE  FF  GG  HH  II                                          Blend or Neat Resin From Example:                                                                 T   U   V   W   D                                           __________________________________________________________________________     Polyphthalamide/Polyphenylene                                                                     100/0                                                                              90/10                                                                              50/50                                                                              10/90                                                                              0/100                                       Sulfide (wt %)                                                                 UTS (kg/cm.sup.2)  1980                                                                               2106                                                                               1613                                                                               1324                                                                               1423                                        Elongation at Break (%)                                                                           3.9 4.3 3.1 2.4 2.7                                         Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                   101 105 110 111 111                                         Flexural Strength (kg/cm.sup.2)                                                                   2931                                                                               3058                                                                               2177                                                                               2071                                                                               2071                                        Notched Izod (cm-kg/cm)                                                                           13.1                                                                               12.5                                                                               11.4                                                                               12.0                                                                               10.4                                        HDT @ 264 psi (°C.)                                                                        129 130 142 267 267                                         Mold Temperature (°C.)                                                                     104 104 104 104 104                                         Barrel Temperature (°C.)                                                   Rear Zone       277 277 277 277 277                                            Front Zone      282 282 282 282 282                                            Nozzle          282 282 282 282 282                                         __________________________________________________________________________

EXAMPLES 32-34

The procedure of EXAMPLES 29-31 was repeated using the blends and neat resins of EXAMPLES 26-28; results and molding conditions are shown in TABLE 17.

                                      TABLE 17                                     __________________________________________________________________________     Example            JJ  32  33  34  KK                                          Blend or Neat Resin From Example:                                                                 0   26  27  28  D                                           __________________________________________________________________________     Polyphthalamide/Polyphenylene                                                                     100/0                                                                              90/10                                                                              50/50                                                                              10/90                                                                              0/100                                       Sulfide (wt %)                                                                 UTS (kg/cm.sup.2)  1733                                                                               2015                                                                               1219                                                                               1381                                                                               1381                                        Elongation at Break (%)                                                                           3.3 3.9 2.2 2.4 2.5                                         Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                   92.8                                                                               98.1                                                                               107 112 112                                         Flexural Strength (kg/cm.sup.2)                                                                   2684                                                                               2895                                                                               1994                                                                               2163                                                                               2015                                        Notched Izod (cm-kg/cm)                                                                           14.7                                                                               14.7                                                                               17.4                                                                               13.6                                                                               13.1                                        HDT @ 264 psi (°C.)                                                                        291 289 272 266 269                                         Mold Temperature (°C.)                                                                     104 104 104 104 104                                         Barrel Temperature (°C.)                                                Rear Zone          310 293 293 293 277                                         Front Zone         316 304 304 304 282                                         Nozzle             316 304 304 304 282                                         __________________________________________________________________________

EXAMPLE 35

This example demonstrates improved thermal endurance of the invented blends relative to the neat polyphthalamide component thereof. The polyphthalamide used in this example as a control and to prepare a blend with ten weight percent Ryton P6 polyphenylene sulfide was prepared essentially as in EXAMPLE 1 from terephthalic acid, isophthalic acid and adipic acid, in a mole ratio of 65:25:10 and hexamethylene diamine. Elemental analysis of the polyphenylene sulfide showed 23.6 weight percent sulfur. The polyphthalamide had the following ash and elemental analyses for sulfur and copper: Ash content (%) 34.8; S content (ppm) <10; Cu content ppm 380

A 33 weight percent glass fiber-filled blend of 90 weight percent polyphthalamide and ten weight percent polyphenylene sulfide was prepared in two steps by extrusion compounding. In a first step, 2700 grams of the polyphthalamide, in the form of pellets, were blended with 300 grams of the polyphenylene sulfide, 13.5 grams talc, 16.1 grams potassium iodide, and 415 grams cupric acetate by tumbling. The blended mixture was rear fed to a ZSK-30 twin screw extruder at a rate of 10.3 kg/hr. The extruder had six independently controlled temperature zones. The temperature set points and actual zone temperatures, beginning at Zone 1 (the feed port) and ending at Zone 6 (the die) were as follows:

    ______________________________________                                                  Zone Temperature (°C.)                                                  1      2        3    4      5    6                                    ______________________________________                                         Set      149    310      310  299    299  310                                  Actual   192    276      300  299    299  293                                  ______________________________________                                    

The recorded melt temperature was 307° C., screw torque was 55% and die pressure was 16.9 kg/cm². Screw speed was 100 rpm. The extruded strand was tan in color.

The strand was cut into pellets by a mechanical chopper. Pellet bulk density was 0.72 g/cm³.

In a second step the blend was compounded with 33 weight percent glass fibers, identified as PPG 3540 obtained from PPG Industries, Inc., which were added to the melted blend through an open port in the third heating zone of the ZSK-30 twin screw extruder. The temperature profile for this extrusion was:

    ______________________________________                                                  Zone Temperature (°C.)                                                  1      2        3    4      5    6                                    ______________________________________                                         Set      288    321      327  324    324  319                                  Actual   274    310      307  318    324  316                                  ______________________________________                                    

Screw rpm was 100, torque was 65%, die pressure was 21.8 kg/cm² and melt temperature was 330° C. The tan, extruded strand was chopped into pellets with a bulk density of 0.35 g/cm³. Ashing and elemental analysis of the resulting filled blend gave the following results: Ash content (%) 32.9; S content (%) 1.63; Cu content (ppm) 370

The resin was molded into Type IV tensile specimens in an Arburg, Model 221 E injection molding machine. The initial tensile strength was 2200 kg/cm². The tensile specimens were thermally aged in groups of five at 220° C. for up to 1008 hours. The tensile strength of each group after aging was determined. These results, together with results for test bars prepared and aged in like manner from the glass fiber filled polyphthalamide without polyphenylene sulfide, are shown below.

    ______________________________________                                                  % Retained Tensile Strength                                                    EXAMPLE 35                                                            Time     (90/10 Polyphthalamide                                                                         Control                                               (hours)  Polyphenylene Sulfide)                                                                         (Polyphthalamide)                                     ______________________________________                                         0        100             100                                                   168      87.2            76.3                                                  336      66.1            64.8                                                  504      61.3            56.6                                                  672      55.9            53.8                                                  720      57.5            --                                                    744      57.8            52.1                                                  840      50.2            47.3                                                  1008     43.1            43.1                                                  ______________________________________                                    

From these thermal aging results the time to 50% retention of tensile strength (hereinafter "F-50") was interpolated, using both cubic polynomial and exponential fits of the data, as follows:

    ______________________________________                                                      Cubic             Exponential                                                  F-50              F-50                                                         (hours) r         (hours)                                                                              r                                         ______________________________________                                         EXAMPLE 35   881     .989      840   .975                                      Control      810     .998      768   .974                                      ______________________________________                                    

where r is the correlation coefficient. Both treatments of the data demonstrate that the resin containing the polyphenylene sulfide had about a 10% longer F-50 at 220° C.

EXAMPLE 36

A second 90/10 polyphthalamide/polyphenylene sulfide blend was prepared using the same procedures and materials as described above, except that the polyphenylene sulfide used was Ryton P4, which had been advanced in molecular weight by solid state polymerization for 16 hours at 238° C. Compounding conditions for the first pass through the extruder were as follows:

    ______________________________________                                                  Zone Temperature (°C.)                                                  1      2        3    4      5    6                                    ______________________________________                                         Set      149    310      310  299    299  310                                  Actual   184    288      299  299    299  305                                  ______________________________________                                    

Torque was 60%, die pressure was 12 kg/cm², screw rpm was 100, melt temperature was 314° C. and feed rate was 10.3 kg/hr. Pellet bulk density was 0.70 g/cm³. The pellets were tan in color.

The conditions for the second extrusion pass were as follows:

    ______________________________________                                                  Zone Temperature (°C.)                                                  1      2        3    4      5    6                                    ______________________________________                                         Set      288    321      327  324    324  319                                  Actual   271    304      310  316    318  313                                  ______________________________________                                    

The melt temperature was 319° C., and the screw speed was 100 rpm.

Ash and elemental analysis of the blend the gave following results: Ash content (%) 35.8; S content (%) 1.74; Cu content (ppm) 330.

Type I tensile specimens of this sample were thermally aged at 220° C. for 120 hours with the blend from EXAMPLE 35 and the control used in the example. The initial and percent retained tensile strengths were as follows:

    ______________________________________                                                          Tensile Strength                                                               Initial  Retained                                                              (kg/cm.sup.2)                                                                           (%)                                                  ______________________________________                                         EXAMPLE 36       2140     86                                                   EXAMPLE 35       2070     89                                                   CONTROL          2400     83                                                   ______________________________________                                    

Examples 37-42

Blends comprising polyphenylene sulfide with other polyphthalamides were prepared, molded and tested. Polyphthalamide D, employed in Examples 37-39 and Control LL, is a hexamethylene terephthalamide/adipamide copolymer having a terephthalic acid/adipic acid ratio of 65/35. Polyphthalamide E, employed in Examples 40-42 and Control MM, is a copolymer of terephthalic acid with a mixture of hexamethylene diamine and its isomer, 2-methylpentamethylene diamine in a 1:1 weight ratio.

The polyphthalamides were prepared substantially following the process outlined in U.S. Pat. No. 4,831,108; the process is exemplified herein as Example 1. Blends comprising polyphthalamide and Ryton P-4 grade of polyphenylene sulfide at three levels together with 35 wt % (based on total composition) of glass fiber were compounded using a 40 mm twin-screw, corotating, vacuum-vented Werner-Pfleiderer ZSK extruder, using a vacuum of 27 in. Hg applied to the port at zone 7, by feeding the glass fiber gravimetrically to the port at zone 5 using a side-arm feeder. The actual temperatures in the extruder barrel ranged from 280° to 370° C. and a die temperature of 345° C., giving a melt temperature of 359°-365° C. Throughput rates were generally 100-200 lbs/hr, the lower rates being employed for the blends with higher levels of polyphenylene sulfide. Test specimens were injection molded using a 75 ton New Britain injection molding machine. The melt temperatures (actual) were in the range 328°-335° C. and the mold temperatures (actual) were in the range 148°-165° C.

The polyphenylene sulfide control specimen NN was prepared by compounding a commercially-obtained PPS resin containing 40 wt % fiberglass with neat resin from the same source, substantially following the procedures outlined above, to provide compositions and test specimens having 35 wt % glass fiber.

It was observed during the injection molding of the various glass-filled blends that the injection pressures decreased as the proportion of PPS resin in the blend increased. The injection pressure used for molding glass-filled PPA-D resin control specimens was 1760 psi, while for the 70/30 blend the injection pressure was 1250 psi, and for the 50/50 blend the injection pressure was 1185 psi. Similarly, the injection pressure used for molding glass- filled PPA-E resin control specimens was 1700 psi, while for the 70/30 blend the injection pressure was 1520 psi, and for the 50/50 blend the injection pressure was 1200 psi. The control specimens molded from the glass-filled PPS resin required injection pressures of 1260 psi.

The mechanical properties are summarized in Table 18 and Table 19.

                                      TABLE 18                                     __________________________________________________________________________     Blend Example      LL  37  38  39  NN                                          __________________________________________________________________________     PolyphthalamideD/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 UTS (kg/cm.sup.2)  1901                                                                               1873                                                                               1830                                                                               1654                                                                               1267                                        Elongation at Break (%)                                                                           2.1 2.0 1.8 1.4 1.2                                         Tensile Modulus (× 10.sup.3 kg/cm.sup.2)                                                    107 111 120 147 127                                         Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                   113 119 124 138 143                                         Flexural Strength (kg/cm.sup.2)                                                                   2781                                                                               2809                                                                               2471                                                                               2161                                                                               1654                                        Izod (cm-kg/cm)                                                                            notched                                                                               8.2 8.4 8.5 6.9 7.7                                                     no-notch                                                                              74.4                                                                               66.8                                                                               50.5                                                                               34.7                                                                               29.3                                        HDT @ 264 psi (°C.)                                                                        307 301 294 277 266                                         __________________________________________________________________________

                                      TABLE 19                                     __________________________________________________________________________     Blend Example      MM  40  41  42  NN                                          __________________________________________________________________________     PolyphthalamideE/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 UTS (kg/cm.sup.2)  2245                                                                               2154                                                                               1661                                                                               1535                                                                               1267                                        Elongation at Break (%)                                                                           2.8 2.8 1.7 1.4 1.2                                         Tensile Modulus (× 10.sup.3 kg/cm.sup.2)                                                    109 109 111 123 127                                         Flexural Modulus (× 10.sup.3 kg/cm.sup.2)                                                   108 113 122 130 143                                         Flexural Strength (kg/cm.sup.2)                                                                   3029                                                                               2826                                                                               2031                                                                               1999                                                                               1654                                        Izod (cm-kg/cm)                                                                            notched                                                                               8.7 7.5 5.9 5.9 7.7                                                     no-notch                                                                              77.6                                                                               66.8                                                                               38.6                                                                               23.9                                                                               29.3                                        HDT @ 264 psi (°C.)                                                                        266 258 262 262 266                                         __________________________________________________________________________

The blends of Examples 37-42 and the corresponding controls were subjected to aging in antifreeze and in methanol/fuel mixtures to evaluate chemical resistance in these aggressive solvent mixtures. The antifreeze mixture was a 50/50 vol./vol. mixture of ethylene glycol and water. The methanol/fuel mixture was standard test mixture CM-85, a mixture of 50 ml of toluene, 850 ml of methanol and 0.85 ml of water, with 0.005 g sodium chloride and 0.050 ml formic acid per liter of solution. The specimens were immersed in the liquid mixtures and held at the specified test temperature (135° C. for the antifreeze mixture, 60° C. for the methanol/fuel mixture) for the test period. Specimens were withdrawn in groups of five at the pre-determined intervals and tested for tensile strength to demonstrate resistance (or lack of resistance) to the solvents. The data are reported in Tables 20-23.

                                      TABLE 20                                     __________________________________________________________________________     Resistance to CM-85 Solution at 60° C.                                  Blend Example      LL  37  38  39  NN                                          __________________________________________________________________________     PolyphthalamideD/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 Days exposure at 60°C.                                                                     retained (%) (UTS, kg/cm.sup.2)                              0*                100 100 100 100 100                                                            (1901)                                                                             (1872)                                                                             (1830)                                                                             (1654)                                                                             (1267)                                      2                  72  77  79  92  101                                         5                  59  64  66  86  99                                          8                  61  65  65  84  102                                         __________________________________________________________________________      Notes: *dry, as molded, test specimen                                    

                                      TABLE 21                                     __________________________________________________________________________     Resistance to CM-85 Tolution at 60° C.                                  Blend Example      MM  40  41  42  NN                                          __________________________________________________________________________     PolyphthalamideE/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 Days exposure at 60° C.                                                                    retained (%) (UTS, kg/cm.sup.2)                              0*                100 100 100 100 100                                                            (2246)                                                                             (2154)                                                                             (1683)                                                                             (1534)                                                                             (1267)                                      2                  85  86  87  99  101                                         5                  76  78  81  97  99                                          8                  70  72  76  96  102                                         __________________________________________________________________________      Notes: *dry, as molded, test specimen                                    

                                      TABLE 22                                     __________________________________________________________________________     Resistance to Ethylene Glycol/water (50/50) Solution at 135° C.         Blend Example      LL  37  38  39  NN                                          __________________________________________________________________________     PolyphthalamideE/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 Days exposure at 60° C.                                                                    retained (%) (UTS, kg/cm.sup.2)                              0*                100 100 100 100 100                                                            (1901)                                                                             (1872)                                                                             (1830)                                                                             (1654)                                                                             (1267)                                      2                  28  35  35  61  87                                          5                  28  26  35  32  75                                          8                  29  28  27  31  66                                          __________________________________________________________________________      Notes: *dry, as molded, test specimen                                    

                                      TABLE 23                                     __________________________________________________________________________     Resistance to Ethylene Glycol/water (50/50) Solution at 135° C.         Blend Example      MM  40  41  42  NN                                          __________________________________________________________________________     PolyphthalamideE/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 Days exposure at 60° C.                                                                    retained (%) (UTS, kg/cm.sup.2)                              0*                100 100 100 100 100                                                            (2246)                                                                             (2154)                                                                             (1683)                                                                             (1534)                                                                             (1267)                                      2                  58  78  77  89  87                                          5                  42  58  51  69  75                                          8                  35  47  36  49  66                                          __________________________________________________________________________      Notes: *dry, as molded, test specimen                                    

The melt rheology of the blends of Examples 37-42 and the corresponding controls was determined at 335° C., using a Kayeness Galaxy® capillary rheometer fitted with a die with an entrance angle of 120°, having a length of 0.80 in. and a diameter of 0.04 in. The rheology data are summarized in the following Table 24 and 25.

                                      TABLE 24                                     __________________________________________________________________________     Melt Rheology at 335° C.                                                Blend Example      LL  37  38  39  NN                                          __________________________________________________________________________     PolyphthalamideD/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 Shear rate (sec.sup.-1)                                                        50                 7750                                                                               7220                                                                               5000                                                                               4520                                                                               6990                                        100                4720                                                                               4260                                                                               3000                                                                               2740                                                                               4400                                        500                1770                                                                               1680                                                                               1380                                                                               1210                                                                               1920                                        1000               1100                                                                               1200                                                                               950 910 1390                                        2500               750 800 650 610 880                                         3500               820 730 590 550 750                                         __________________________________________________________________________      Notes: Shear rates are apparent values; Melt viscosities are in poise.   

                                      TABLE 25                                     __________________________________________________________________________     Melt Rheology at 335° C.                                                Blend Example      MM  37  38  39  NN                                          __________________________________________________________________________     PolyphthalamideE/Polyphenylene                                                                    100/0                                                                              85/15                                                                              70/30                                                                              50/50                                                                              0/100                                       Sulfide (wt %)                                                                 Shear rate (sec.sup.-1)                                                        50                 7660                                                                               6650                                                                               4400                                                                               3810                                                                               6990                                        100                5710                                                                               4660                                                                               298o                                                                               2540                                                                               4400                                        500                3160                                                                               2450                                                                               1490                                                                               1080                                                                               1920                                        1000               2360                                                                               1780                                                                               1110                                                                               830 1390                                        2500               1480                                                                               1160                                                                               760 560 880                                         3500               1150                                                                               940 660 500 750                                         __________________________________________________________________________      Notes: Shear rates are apparent values; Melt viscosities are in poise.   

It will be apparent from a comparison of the melt rheology of either of the two resin components with the rheology of each of the blends that the melt viscosity of the polyterephthalamide is reduced by adding the polyphenylene sulfide. This rheology behavior is consistent with the reduction in injection pressure observed for the blends, as noted herein above, and reflects a significant improvement in the processability for these blends over the corresponding glass-filled polyphthalamide.

When test specimens molded from the blends of Examples 37-42 are subjected to thermal aging substantially following the procedures in Example 35, the thermal endurance of the test specimens, as shown by comparing the retention of tensile properties for the blends with the polyphthalamide controls, will generally be seen to be improved by the addition of polyphenylene sulfide.

The invention will thus be seen to be a blend comprising a polyarylene sulfide and a polyterephthalamide wherein the polyterephthalamide component, when filled with glass fibers, has a heat deflection temperature at 264 psi, according to ASTM D-648, above about 240° C. The blends will preferably contain from about 10 to about 90 weight percent of the polyarylene sulfide component based on the weight of polyphthalamide and polyarylene sulfide and, when filled, will contain from about 10 to about 60 wt % of the filler. Generally, the polyphthalamide component may be characterized as comprising terephthalamide units, and may optionally include additional carboxylamide units, preferably selected from isophthalamide units and adipamide units. The proportion of terephthalamide units will lie in the range of from 40 to 100 mole % and, when present, from 0 to 35 mole % isophthalamide units and from 0-60 mole % adipamide units.

Further variations and modifications will be readily apparent to those skilled in the compounding arts, including the further incorporation of stabilizers, dyes, pigments, lubricants and processing aids and the like as commonly practiced in the resin arts, and these modifications will be understood as included within the scope of the invention set forth herein and in the appended claims. 

We claim:
 1. A composition comprising from about 10 to about 90 wt % of (i) a polyphthalamide comprising terephthalamide units, said polyphthalamide when filled with 33 weight percent glass fibers and molded having a heat deflection temperature at 264 psi according to ASTM D-648 of at least about 240° C.; and from about 90 to about 10 wt % of (ii) a polyphenylene sulfide based on the total weight of said components (i) and (ii).
 2. The composition of claim 1 further comprising a filler.
 3. A composition comprising from about 10 to about 90 wt % of a polyphthalamide having a heat deflection temperature at 264 psi according to ASTM D-648 of at least about 240° C. when filled with 33 weight percent glass fibers and molded, said polyphthalamide comprising the following recurring units: ##STR2## wherein the mole ratio of units A, B and C is about 40-100:0-35:0-60 and wherein R, R₁ and R₂ are independently divalent hydrocarbyl radicals; andfrom about 90 to about 10 wt % of a polyphenylene sulfide, the proportion of each said component being based on combined weight of said polyphthalamide and said polyphenylene sulfide.
 4. The composition of claim 3 wherein R, R₁ and R₂ comprise hexamethylene.
 5. The composition of claim 3 wherein the polyphthalamide consists of units A and C.
 6. The composition of claim 3 wherein the mole ratio of dicarboxylic acid moieties in the units A, B and C is about 65-90:25-0:35-5.
 7. The composition of claim 3 further comprising from about 10 to about 60 weight percent glass fiber, based on total weight of the composition.
 8. A composition comprising from about 10 to about 90 wt % of a polyphthalamide having a heat deflection temperature at 264 psi according to ASTM D-648 of at least about 240° C. when filled with 33 weight percent glass fibers and molded, said polyphthalamide comprising at least two different recurring units selected from the group consisting of the following recurring units: ##STR3## wherein R, R₁ and R₂ are independently divalent hydrocarbyl radicals; andfrom about 90 to about 10 wt % of a polyphenylene sulfide, the proportion of each said component being based on combined weight of said polyphthalamide and said polyphenylene sulfide.
 9. The composition of claim 8 wherein the mole ratio of units A, B and C is about 40-99:0-35:0-60.
 10. The composition of claim 8 wherein the mole ratio of dicarboxylic acid moieties in the units A, B and C is about 50-95:25-0:35-5.
 11. The composition of claim 8 wherein the mole ratio of dicarboxylic acid moieties in the units A, B and C is about 65-90:25-0:35-5.
 12. The composition of claim 8 wherein the polyphthalamide consists of units A and C.
 13. The composition of claim 8 wherein the mole ratio of dicarboxylic acid moieties in the units A, B and C is about 50-90:0:50-10. 